96TSC SAC387 Solder

E-Qual 96TSC is a high-performance, lead-free solder alloy designed as a direct substitute for traditional tin/lead solders in all electronics assembly operations. It is an all-around, lead-free alternative proven in production use. This eutectic alloy offers a precise melting point and exceptional joint performance.

Key Features

- Lead-Free Alternative: Eliminates lead handling and waste management hazards, ensuring RoHS compliant assemblies.

- Eutectic Alloy: Features a single melting point of 217°c (no melting range) for consistent results.

- High Performance: Soldered joints perform as well as tin/lead joints in most respects.

- Compatibility: Compatible with all flux types.

- Reliability: Offers excellent tensile strength (52N/mm²) and creep strength (>300h with 180°c load).

Product Description

E-Qual 96TSC alloy is the lowest melting, high-tin, lead-free alloy without undesirable additions. While equipment settings will require adjustment due to its melting point being 34°c higher than tin/lead eutectic alloy, the resulting soldered joints provide reliable performance. Regular analysis of the solder bath content is recommended to ensure optimum performance and prevent impurity build-up. DKL Metals offers a free bath analysis program for this purpose to our customers. Copper levels can often be controlled by topping up the bath with E-Qual 96TS copper-free alloy.

Technical Specifications Summary

- Density 7.4g/cm³
- Melting Point 217°c
- Electrical conductivity 0.15µΩm

Availability

E-Qual 96TSC is made from fully traceable batches of virgin metals within an ISO9001:2000 approved Quality Management System.

It is available in various styles:

- Bar: 1kg weight, 20kg cartons
- Autofeed Ingot: 4kg weight & 2kg weight, 20kg cartons
- Chunks: 20kg tub
- Wire: 4kg reel (3mm diameter)